S355J2W

2023-05-15 08:48:00 來源：鋼鐵之家閱讀量：0

牌號(hào)	S355J2W
歐標(biāo)鋼號(hào)	1.8965
對(duì)應(yīng)標(biāo)準(zhǔn)	EN 10025-5-2019 熱軋結(jié)構(gòu)鋼-第5部分：耐候結(jié)構(gòu)鋼 Hot rolled products of structural steels-Part 5: Technical delivery conditions for structural steels with improved atmospheric corrosion resistance
歸類	合金鋼
標(biāo)簽	耐候結(jié)構(gòu)鋼鎮(zhèn)靜鋼

S355J2W 化學(xué)元素成分含量(%)

	成分	C	Si	Mn	P	S	Cr	Ni ^③	Cu	Mo ^③	Zr ^③
長(zhǎng)形產(chǎn)品	最小值	-	-	0.5	-	-	0.4	-	0.25	-	-
長(zhǎng)形產(chǎn)品	最大值	0.16	0.5	1.5	0.03	0.03	0.8	0.65	0.55	0.3	0.15

	成分	C	Si	Mn	P	S	Cr	Ni ^③	Cu	Mo ^③	Zr ^③
	最小值	-	-	0.5	-	-	0.4	-	0.25	-	-
	最大值	0.16	0.5	1.5	0.035	0.035	0.8	0.65	0.55	0.3	0.15

①FN=rimming steels not permitted(不允許沸騰鋼)；FF=fully killed steel(完全鎮(zhèn)靜鋼)
②The steels contain at least one of the following elements: Al total≥0.02%，Nb:0.015~0.06%，V:0.02~0.12%，Ti:0.02~0.1%。If these elements are used in combination, at least one them shall be present with the minimum content indicated。(鋼應(yīng)至少含有下列元素之一:Al總含量為≥0.020%，Nb:0.015 ~ 0.060%，V:0.02 ~ 0.12%，Ti:0.02 ~ 0.10%。如果將這些元素組合使用，其中至少有一種元素應(yīng)具有所示的最低含量。)
③鋼中Ni、Mo、Zr含量可達(dá)的最大值
④當(dāng)Si的最低含量為0.15%時(shí)，Cr含量可降至0.37%

碳當(dāng)量計(jì)算

S355J2W 機(jī)械性能

厚度 t mm	抗拉強(qiáng)度 σ_b Mpa	屈服點(diǎn) σ_s Mpa	斷后伸長(zhǎng)率或延伸率 δ %
t＜3	510~680	≥355	見備注
3≤t≤16	470~630	≥355	≥22
16＜t≤40	470~630	≥345	≥22
40＜t≤63	470~630	≥335	≥21
63＜t≤80	470~630	≥325	≥20
80＜t≤100	470~630	≥315	≥20
100＜t≤150	450~600	≥295	≥18

①公稱厚度1.5＜t≤2時(shí)，斷后延伸率δ≥16
②公稱厚度2＜t≤2.5時(shí)，斷后延伸率δ≥17
③公稱厚度2.5＜t＜3時(shí)，斷后延伸率δ≥18

近似對(duì)照表結(jié)構(gòu)、壓力容器和工程鋼

日本	美國(guó)	德國(guó)	歐標(biāo)
JIS	ASTM	DIN EN/DIN	EN	數(shù)字牌號(hào)
SMA50CP	A709-50W	WTSt52-3	S355J2W S355J2G2W①	1.8965