AMS 5596

2023-05-17 18:33:01 來(lái)源：鋼鐵之家閱讀量：0

牌號(hào)	AMS 5596
對(duì)應(yīng)標(biāo)準(zhǔn)	SAE AMS 5596 M-2017 鎳合金，耐腐蝕和耐熱，薄板，帶材，箔材和板材 Nickel Alloy, Corrosion and Heat-Resistant, Sheet, Strip, Foil and Plate, 52.5Ni - 19Cr - 3.0Mo - 5.1 Cb (Nb) - 0.90Ti - 0.50AI - 18Fe, Consumable Electrode Remelted or Vacuum Induction Melted 1775 °F (968°C) Solution Heat Treated
歸類	合金鋼

AMS 5596 化學(xué)元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	Ti	Nb	B	Co	Al	Ta	更多
最小值	-	-	-	-	-	17	50	-	2.8	0.65	4.75	-	-	0.2	-	Fe余量
最大值	0.08	0.35	0.35	0.015	0.015	21	55	0.3	3.3	1.15	5.5	0.006	1	0.8	0.05	Fe余量

AMS 5596 機(jī)械性能

厚度 t mm	熱處理或狀態(tài)	抗拉強(qiáng)度 σ_b Mpa	屈服點(diǎn) σ_s Mpa	斷后伸長(zhǎng)率或延伸率 δ %	硬度 HBW
t≤0.01	As Solution	≤965		report
0.01＜t≤0.1874	As Solution	≤965		≥30	HRB ≤102
0.1874＜t≤1.00	As Solution	≤1034		≥30	HRC ≥25
t≤0.25	After Precipitation/At Room Temperature	≥1241	≥1034	report
0.25＜t≤25.4	After Precipitation/At Room Temperature	≥1241	≥1034	≥12
t≤0.64	After Precipitation/At 649 °C	≥965	≥793	≥5
0.64＜t≤25.4	After Precipitation/At 649 °C	≥1000	≥827	≥5

注1：Elongation in 2 Inches or 4D.
注2：At Room Temperature：Determined in accordance with ASTM E8/E8M.
注3：At 1200 °F (649 °C)：Determined in accordance with ASTM E21 on specimens heated to 1200 °F 土5 °F (649 °C 士3 °C) , held at heat for not less than 20 minutes before testing, and tested at 1200 ° F 士5 °F (649 °C 士3 °C) .

注：本資料來(lái)源于互聯(lián)網(wǎng)的公開資源整理，我們不保證這些資料的準(zhǔn)確性、完整性和適用性。這些資料僅供您參考，不應(yīng)用于任何商業(yè)用途或決策依據(jù)。本資料所記載的技術(shù)信息是說明產(chǎn)品的代表性特點(diǎn)和性能的參考值，對(duì)于因誤用或不當(dāng)使用本資料所記載的信息等而造成的損害恕難承擔(dān)責(zé)任，敬請(qǐng)周知。