P305GH

2023-05-17 17:37:52 來源：鋼鐵之家閱讀量：0

牌號	P305GH
歐標鋼號	1.0436
對應(yīng)標準	EN 10222-2-2017 壓力用途用鋼制鍛件第2部分具有高溫特性的鐵素體和馬氏體鋼 Steel Forgings for Pressure Purposes. Part 2:Ferritic and Martensitic Steels with Specified Elevated Temperature Properties
歸類	碳鋼

P305GH 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	Ti	V	Nb	更多
最小值	0.15	-	0.9	-	-	-	-	-	-	-	-	-	Cr+Cu+Mo+Ni≤0.70；碳當量≤0.47
最大值	0.2	0.4	1.6	0.025	0.015	0.3	0.3	0.3	0.08	0.03	0.02	0.01	Cr+Cu+Mo+Ni≤0.70；碳當量≤0.47

碳當量計算

P305GH 機械性能

厚度 t mm	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷后伸長率或延伸率 δ %	沖擊吸收能量 KV2 J
t≤35	490~610	≥305	I：≥22，tr/t：≥20	I：≥48，tr/t：≥27
35＜t≤160	490~610	≥280	I：≥22，tr/t：≥20	I：≥48，tr/t：≥27
t≤70	510~630	≥285	I：≥22，tr/t：≥20	I：≥48，tr/t：≥27

① I = longitudinal to main forging directions；tr = transverse to main forging directions；t = tangential.
② Maximum room temperature for the impact test is 20 °C. By option, impact testing may be carried out at 0°C, with the condition to fulfil the impact values as stated in this table.
③ Until the yield point criteria are harmonized in the various national codes, determination of ReH may be replaced by determination of Rp0.2. In this case Rp0.2 values are 10 MPa lower for ReH values up to 355 MPa and 15 MPa lower for ReH values greater than 355 MPa.

熱處理制度（僅供參考）

N = normalized; QT= quenched and tempered; NT= normalized and tempered. a = air; f = furnaced; o = oil; w = water or water based medium.

注：本資料來源于互聯(lián)網(wǎng)的公開資源整理，我們不保證這些資料的準確性、完整性和適用性。這些資料僅供您參考，不應(yīng)用于任何商業(yè)用途或決策依據(jù)。本資料所記載的技術(shù)信息是說明產(chǎn)品的代表性特點和性能的參考值，對于因誤用或不當使用本資料所記載的信息等而造成的損害恕難承擔責任，敬請周知。

精品国产专区91在线图片,一本一本久久a久久,国产sm精品调教网站,久久青草一区二区三区

P305GH

熱處理制度（僅供參考）