302C25

2023-05-17 15:07:54 來源：鋼鐵之家閱讀量：0

牌號	302C25
對應標準	BS 3100-1991 一般工程用鑄鋼件 Specification for Steel castings for general engineering purposes
歸類	鑄鋼
性能	耐腐蝕
標簽	奧氏體不銹鑄鋼有磁性

302C25 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni
最小值	-	-	-	-	-	17	8
最大值	0.12	1.5	2	0.04	0.04	21	-

碳當量計算

302C25 機械性能

熱處理或狀態(tài)	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷后伸長率或延伸率 δ %
ST(1000°C~1100°C)	≥480	1% proof stress Rp1.0 min ≥240	≥26

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

1 近似對照表耐蝕鑄鋼（不銹鋼鑄件）

中國	日本	美國	德國		法國	英國
GB	JIS	ASTM	DIN EN/DIN	W-Nr.	NF EN/NF	BS EN/BS
ZG1Cr18Ni9	SUS12	CF20	G-X10CrNi 18 8	1.4312	Z10CN18.9M	302C25

2 近似對照表耐熱鑄鋼和耐熱合金鑄件

中國	日本	德國		法國	俄羅斯	英國
GB	JIS	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG1Cr18Ni9	SCS12 SCS13A	G-X10CrNi18 8	1.4312	Z10CN18.9M	10Х18Н9Л	302C25

注：本資料來源于互聯(lián)網(wǎng)的公開資源整理，我們不保證這些資料的準確性、完整性和適用性。這些資料僅供您參考，不應用于任何商業(yè)用途或決策依據(jù)。本資料所記載的技術信息是說明產(chǎn)品的代表性特點和性能的參考值，對于因誤用或不當使用本資料所記載的信息等而造成的損害恕難承擔責任，敬請周知。