AW3

2023-05-17 16:29:47 來源：鋼鐵之家閱讀量：0

牌號	AW3
對應(yīng)標(biāo)準(zhǔn)	BS 3100-1991 一般工程用鑄鋼件 Specification for Steel castings for general engineering purposes
歸類	鑄鋼
標(biāo)簽	碳鋼鑄鋼耐磨和表面硬化用鑄鋼

AW3 化學(xué)元素成分含量(%)

成分	C	Si	Mn	P	S	Cr ^②	Ni ^②	Cu ^②	Mo ^②	其他合計
最小值	0.5	-	-	-	-	-	-	-	-	-
最大值	0.6	0.6	1	0.05	0.05	0.3	0.4	0.3	0.15	0.8

其他單個或其他合計化學(xué)成分包括表中未指定值的化學(xué)成分。只有在假定存在或在常規(guī)分析中，且有跡象表明其成分將超過規(guī)定值的情況下，才應(yīng)進(jìn)行分析。

①碳含量每降低0.01%，最大錳含量則增加0.04%，允許最大錳含量到1.1%
②殘余元素。

碳當(dāng)量計算

AW3 機械性能

熱處理或狀態(tài)	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷后伸長率或延伸率 δ %
A或N或N+T	≥690	≥370	≥8

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

近似對照表鑄鋼

中國	日本	德國		英國
GB	JIS	DIN EN/DIN	W-Nr.	BS EN/BS
ZG40Mn	SCMn3	GS-40Mn5	1.1168	AW3

注：本資料來源于互聯(lián)網(wǎng)的公開資源整理，我們不保證這些資料的準(zhǔn)確性、完整性和適用性。這些資料僅供您參考，不應(yīng)用于任何商業(yè)用途或決策依據(jù)。本資料所記載的技術(shù)信息是說明產(chǎn)品的代表性特點和性能的參考值，對于因誤用或不當(dāng)使用本資料所記載的信息等而造成的損害恕難承擔(dān)責(zé)任，敬請周知。